LD2 HTC 1000 18160 CC1198-18
high toughness, high light transmission, processing stabilised, injection. Applications: Covers & Panels.
Specifications
Mechanical Properties
| Flexural Modulus | 1600 MPa |
| Tensile Modulus | 1600 MPa |
| Tensile Stress at Yield | 45 MPa |
| Tensile Elongation at Break | 125 % |
| Notched Charpy Impact (23°C) | 95 kJ/m² |
Physical Properties
| flexural_stress_3.5%_strain | 51 MPa |
| tensile_elongation_at_yield | 6.2 % |
| impact_strength_charpy,_23°c_no_break | kJ/m² |
| impact_strength_charpy,_-40°c_no_break | kJ/m² |
| notched_impact_strength_charpy,_-40°c | 9 kJ/m² |
| shrinkage_24h | 0.4 - 0.7 % |
| Density | 1180 kg/m³ |
| flammability_1.5_mm_hb_clas | s |
| glow_wire_gwfi,_850°c,_1.0mm_passed_-_di | N |
Thermal Properties
| Vicat B | 50 108 °C |
| HDT/A (1.8 MPa) | 84 °C |
| Melt Volume Rate | 15 cm³/10min |
Request Free Sample
First-time customers can receive 500g free sample of LD2 HTC 1000 18160 CC1198-18. Freight collect.
Request a quote
The Experience Behind Every Shipment
Our team brings over 30 years of combined experience in the chemical and plastics industries, with seasoned technical specialists providing full-cycle online support — from material selection and application troubleshooting to processing guidance. Having served 1,000+ clients worldwide and worked inside Western enterprises, we understand your standards, your culture, and your expectations. Fluent in English, grounded in Chinese market expertise, and committed to stable quality, professional technical service, and responsive after-sales support.