LB PA6 2015 14041 GF15 WT1100-14
high stiffness, highly reflective, opaque. Applications: reflectors, light blocking components, Lighting.
Specifications
Mechanical Properties
| Flexural Modulus | 5000 MPa |
| Flexural Strength | 150 MPa |
| Tensile Modulus | 6000 MPa |
| Tensile Elongation at Break | 2 % |
| Charpy Impact Strength (23°C) | 30 kJ/m² |
| Notched Charpy Impact (23°C) | 3 kJ/m² |
Physical Properties
| tensile_strength_at_break | 100 MPa |
| impact_strength_charpy,_-40°c | 30 kJ/m² |
| notched_impact_strength_charpy,_-40°c | 2 kJ/m² |
| dsc_melt_point | 220 °C |
| shrinkage_lengthwise,_24h | 0.3 - 0.5 % |
| shrinkage_lateral,_24h | 0.6 - 0.8 % |
| Density | 1290 kg/m³ |
| tristimulus_value_y10_of_reflection_d=2,0mm | 85 % |
| tristimulus_value_y10_of_transm.,d=0.5mm | 0.9 % |
Thermal Properties
| HDT/A (1.8 MPa) | 196 °C |
Request Free Sample
First-time customers can receive 500g free sample of LB PA6 2015 14041 GF15 WT1100-14. Freight collect.
Request a quote
The Experience Behind Every Shipment
Our team brings over 30 years of combined experience in the chemical and plastics industries, with seasoned technical specialists providing full-cycle online support — from material selection and application troubleshooting to processing guidance. Having served 1,000+ clients worldwide and worked inside Western enterprises, we understand your standards, your culture, and your expectations. Fluent in English, grounded in Chinese market expertise, and committed to stable quality, professional technical service, and responsive after-sales support.